Two-part, moderately fast-curing, hybrid polyurea, spray-applied elastomeric coating. It provides a premium quality, high build, long-life protective coating to concrete and metal substrates on major civil, infrastructure and commercial construction projects. Formulated using the latest polyurea technology, it forms an impenetrable barrier that is resistant to water, many chemicals and wear.
Features and Benefits
Silcor® 780 HI-LP is a low toxicity elastomer system, containing no TDI, MOCA, bitumen or tar-based compounds.
Being polyurea-based, it has good resistance to humidity during application and forms a tough, bubble-free, impermeable coating.
Silcor 780 HI-LP is a simple 100:100 by volume mix ratio system that applies with improved flow out and rapid cure, resulting in a smooth, even coating finish that can be walked on in minutes.
The cured elastomer has high substrate adhesion plus excellent resistance to tear, puncture, chemicals, water and abrasion. Unlike rigid coating materials such as epoxies, vinyl ester, etc, Silcor 780 HI-LP resists post-application reflection cracking in concrete.
- Simple application — fast-cure
- Long life — permanently flexible
- Slower cure provides smooth surface finish
- Resists reflection cracking in concrete
- Suitable for continuous immersion in fresh and salt waters
Silcor 780 HI-LP elastomer system is ideally suited for most areas of protective coating, lining and waterproofing in civil and commercial applications.
Used as a tough, flexible, waterproof membrane and coating, particularly over concrete substrates on:
- Water treatment plants
- Roof decks
- Podium slabs
- Water tanks
- Bridge decks
- Tunnels and underground structures include cut & cover, drill and blast tunneling
Silcor 780 HI-LP is compatible with most stable, suitably prepared rigid substrates, including concrete, steel, aluminium, shotcrete, brick, block, render, fibre cement sheet, plywood and timber.
Silcor 780 HI-LP is designed for application through high-pressure, plural component spray equipment capable of processing polyurea coatings, such as electrical motor pump driven machine and hydraulic pump driven machine.
Silcor 780 HI-LP polyamine component must be agitated before and during use. The isocyanate component does not require agitation.
Typical machine spray settings required for Silcor 780 HI-LP application are:
Material Temperature: 20°C to 25°C
Main Heater Temperature: 60°C to 75°C
Line Heater Temperature: 60°C to 75°C
Spray Pressure: 2200 to 3000 psi
Round pattern spray gun mix chambers will minimise overspray produced considerably.
This product may also be suitable for 1:1 by volume, low-pressure dispensing machines fitted with static mix spray heads. Suitability should be determined by the user prior to application.
|PROPERTY||TYPICAL VALUE||TEST METHOD|
|Mix Ratio - Polyamine : Iso (by volume)||100 : 100||-|
|Polyamine Viscosity (@ 25ºC)||400 - 1000 mPa.s||ASTM D2196|
|Polyamine Specific Gravity (@ 25ºC)||1.03g / mL||ASTM D1475|
|Isocyanate Viscosity (@ 25ºC)||400 - 1000 mPa.s||ASTM D2196|
|Isocyanate Specific Gravity (@ 25ºC)||1.11g / mL||ASTM D1475|
|Gel Time (@ 25ºC)||20 seconds||-|
|Tack Free Time (@ 25ºC)||60 seconds||-|
|% Solids (v/v)||100%||-|
|Recommended Applied Thickness||1.5mm||-|
|Return to Service
- Light Foot Traffic
- Heavy Foot Traffic
- Continuous Water Immersion
- Paving, Topping, Backfill, Landscaping
- Chemical or Abrasion Exposure
|Shore A Hardness (Minimum)||80 ± 5||ASTM D2240|
|Tensile Strength (Minimum)||> 9.0 MPa||ASTM D412|
|Elongation (Minimum)||350%||ASTM D412|
|Taber Abrasion Resistance (Maximum)||220 mg||ASTM D4060|
|Crack Bridging, 2mm||Pass||ASTM C836|
|Pull-Off Strength (Minimum)
- Concrete (Primed) (Substrate Failure Occurred)
- Steel (90μm Blast Profile)
> 2.0 MPa
> 3.0 MPa
Substrates must be clean, dry, free of curing compounds, oil, grease, solvent or other contaminants. Moisture content of concrete must be below 5%.
The following conditions must be achieved prior to and maintained during Silcor 780 HI-LP application.
Ambient Temperature: 5°C to 45°C
Substrate Temperature: 10°C to 60°C
Relative Humidity: 85% maximum
Dew Point: 3°C below substrate
Approximate Wind Speed 10 knots maximum
See project-specific Application Method Statement (AMS) for detailed requirements. Generally, for concrete substrates, use wet, wet-abrasive e.g. high pressure water jet, rotary head water blaster or dry-abrasive blasting e.g. mechanical grinding to remove laitance, etc.
Patch defects using suitable fairing compound.
Fill all joints, cracks, gaps and form angle fillets in internal corners or penetrations with Silcor LM PU sealant.
Blast or mechanically clean steel substrates to a 90μm surface profile.
Prime with Silcor Primer BW N105 at 0.12 - 0.25kg / m2 or Silcor Primer BS at 0.15 - 0.3kg / m2 dependent on substrate condition. Allow to dry approximately 2 to 5 hours depending on ambient conditions and surface porosity.
Apply product in one or more passes to the required dry film thickness. Typically a DFT of 1.5mm is required for waterproof applications and 2.0 to 3.5mm is required for protective coating/lining applications. Specified minimum DFT required will be detailed in GCP’s project-specific AMS..
Where colour stability is required in sun-exposed applications, apply our aliphatic, UV-stable topcoat, Silcor Top Coat 80 where colour stable protection and a non-slip finish is required.
An area smaller than 1m² may be repaired by re-application of Silcor 780 HI-LP as detailed in the relevant Application Method Statement. In space-restricted areas where spray application is not practical, Silcor 580 membrane systems (with Silcor Top Coat 80 finish where UV stability or non-slip finishes are required) can be used, in consultation with your local GCP representative.
Out-grassing and pin-hole formation due to poorly compacted, high porosity or wood float finished concrete after spray application, can be spot patch/touch up the pin-holes with Silcor® LM PU Sealant or epoxy filler.
Clean up liquid leakage or spills before hardening occurs using solvents such as xylene, MEK or acetone.
Silcor 780 HI-LP polyamine and isocyanate components should be stored < 25°C, < 60% RH. Drums must remain tightly sealed against moisture ingress. Under these storage conditions the materials will have a shelf life of 12 months. Storage at temperatures other than detailed can result in degradation and crystallisation in the drum, rendering the materials unusable. Ingress of humidity or water into the drums during storage or use will also make the materials unusable.
1.1kg (1 litre) of Silcor 780 HI-LP system provides coverage of 1m2 at 1.0mm coating thickness. Allow for processing losses, over-spray, etc depending on surface and ambient conditions.
Silcor 780 HI-LP Polyamine: 18.5kg & 200kg drums
Silcor 780 HI-LP Isocyanate: 20kg & 210kg drums
Silcor 780 HI-LP system is not intended for use by other than experienced operators. The data herein requires experience and knowledge to attain correct interpretation and outcome. The user must undertake all relevant tests to determine the suitability for the intended application, as such determination of fitness of purpose for product use is the sole responsibility of the purchaser.
Refer to Silcor 780 HI-LP Material Safety Data Sheet (MSDS).
Operators must have full awareness of the material safety requirements before any work is undertaken.
Silcor 780 HI-LP polyamine component is a mild irritant. Avoid contact with skin or eyes. Silcor 780 HI-LP isocyanate component contains methylenebisphenyl diisocyanate (MDI). It is an irritant and allergic sensitiser to skin and respiratory systems. Avoid contact with skin or eyes. Avoid breathing vapour or spray aerosol.
Silcor 780 HI-LP system spray application must occur in areas with adequate ventilation. Suitable organic vapour respirators or air-fed hoods must be worn during spray operations. Other required PPE includes butyl or nitrile gloves, safety goggles or full-face shield, coveralls and chemically-resistant safety boots.
Health and Safety
In case of spills and accidents, refer to the MSDS of the products or when in doubt contact your local GCP representative.
Always wear protective clothing, gloves and protective goggles when handling chemical products.
For full information, consult the relevant MSDS.
GCP Applied Technologies offers a comprehensive package of quality and proven systems to meet different project and application needs. Contact your local GCP representative for further information.
th.gcpat.com | Thailand customer service: 66 2 030 9700
Australia 1800 855 525 New Zealand +64 9 448 1146 China Mainland +86 21 3158 2888 Hong Kong +852 2675 7898India +91 124 488 5900 Indonesia +62 21 893 4260 Japan +81 3 5226 0231 Korea +82 32 820 0800 Malaysia +60 3 9074 6133 Philippines +63 49 549 7373 Singapore +65 6265 3033 Thailand +66 2 709 4470 Vietnam +84 8 3710 6168
We hope the information here will be helpful. It is based on data and knowledge considered to be true and accurate, and is offered for consideration, investigation and verification by the user, but we do not warrant the results to be obtained. Please read all statements, recommendations, and suggestions in conjunction with our conditions of sale, which apply to all goods supplied by us. No statement, recommendation, or suggestion is intended for any use that would infringe any patent, copyright, or other third party right.
Silcor is a trademark, which may be registered in the United States and/or other countries, of GCP Applied Technologies, Inc. This trademark list has been compiled using available published information as of the publication date and may not accurately reflect current trademark ownership or status.
© Copyright 2017 GCP Applied Technologies, Inc. All rights reserved.
GCP Applied Technologies Inc., 62 Whittemore Avenue, Cambridge, MA 02140, USA
This document is only current as of the last updated date stated below and is valid only for use in Thailand. It is important that you always refer to the currently available information at the URL below to provide the most current product information at the time of use. Additional literature such as Contractor Manuals, Technical Bulletins, Detail Drawings and detailing recommendations and other relevant documents are also available on www.th.gcpat.com. Information found on other websites must not be relied upon, as they may not be up-to-date or applicable to the conditions in your location and we do not accept any responsibility for their content. If there are any conflicts or if you need more information, please contact GCP Customer Service.
Last Updated: 2020-01-16